Presented in this report are the results of stress corrosion cracking testing per ASTM G36 (Standard Practice for Performing Stress-Corrosion Cracking Tests in a. austenitic stainless steel was studied in accordance with the ASTM G The samples were unidirectional cold-rolled up to 60 and 90 percent reduction in. Revised ASTM G36 apparatus. This client had been testing stress corrosion- cracking in metal welds by clamping a QVF 2″ glass pipe fitting to his samples.

Author: Mujinn Dozil
Country: Mozambique
Language: English (Spanish)
Genre: Medical
Published (Last): 6 February 2004
Pages: 295
PDF File Size: 20.56 Mb
ePub File Size: 8.88 Mb
ISBN: 162-7-98543-792-3
Downloads: 2432
Price: Free* [*Free Regsitration Required]
Uploader: Tygosar

No preparation other than deburring and degreasing was performed on the test specimens prior to testing. Deepest crack found on longitudinal cross-section of bare tube. Careful examination is recommended for correct diagnosis of the cause of failure. Corrosion Testing Laboratories, Inc. Quality Assurance Return to Corrosion Testing.

Circumferential cracks with connecting longitudinal crack in base metal of bare tube. Although this test may be performed using various concentrations of magnesium chloride, this procedure covers a test solution held at a constant boiling temperature of It is a method for detecting the effects of composition, heat treatment, surface finish, microstructure, and stress on the susceptibility of these materials to chloride stress corrosion cracking.

Referenced Documents purchase separately The documents listed below are referenced within the subject standard but are not provided as part of the standard. The test may not be relevant to stress-corrosion cracking in polythionic acid or caustic environments.

Referenced Documents purchase separately The documents listed below are referenced within the subject standard but are not provided as part of the standard. Accompanying paperwork states that both types of tube were fabricated from the same heat lot of material. See Section 7 for specific safety precautions. The test specimens were immersed in the boiling solution and supported using the suggested ladder-back cradles. Black lines indicate the approximate location of the outer surface of the tube.

  HIGH VOLTAGE ENGINEERING KUFFEL PDF

The boiling points of aqueous magnesium chloride solutions at one atmosphere pressure as a function of concentration are shown graphically in Fig.

It is a method for detecting the effects of composition, heat treatment, surface finish, microstructure, and stress on the susceptibility of these materials to chloride stress corrosion cracking. Photographs of typical appearance of the cracks on both tubes are shown in Figures 1 and 2. It was decided that cracks in the bare tube could be best examined using a longitudinal cross-section, while the cracks in the finned tube could be best examined using a transverse cross-section.

Crack characteristics were investigated by preparing metallographic sections of the test specimens. However, such correlations may not always be possible. Newark, Delaware USA Regular examination periods for test specimen cracking were scheduled.

This leads to the possibility of confusing stress-corrosion failures with mechanical failures induced by corrosion-reduced net cross sections. See Section 7 for specific safety precautions. t36

It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use. Materials that normally provide acceptable resistance in hot chloride service may crack in this test.

Revised ASTM G36 apparatus

This danger is particularly great when small cross section samples, high applied stress levels, long exposure periods, stress-corrosion resistant alloys, or a combination thereof are being used. Link to Active This link will always route to the current Active version of the standard. Both test specimens were taken off test at 8 hours for examination at low magnification.

  BEHRINGER ULTRADRIVE PRO DCX2496 MANUAL PDF

Link to Active This asttm will always route to the current Active version of the standard. Active view current version of standard. On the finned test specimen, cracks extended down the fins from the outer edge to the tube gg36 in a direction roughly normal to the tube wall; at the tube wall the cracks extended in a short arc both longitudinally and circumferentially, the arcs stopping before the next fin was encountered. Microphotographs of the deepest cracks found ashm the mounted sections are shown in Figures 3 and 4.

The boiling points of aqueous magnesium chloride solutions at one atmosphere pressure as a function of concentration are shown graphically in Fig. Cracking of both test specimens was observed, and the tests were terminated.

Two 2 1-foot long pieces of 0. Return to Corrosion Testing. Test procedures conformed to the referenced ASTM asfm method. Deepest cracks found on transverse cross-section of finned tube. Circumferential cracking of the bare tube test specimen was apparent within the first 8 hours of testing even while the test specimen was on test.

ASTM G36 – 94(2013)

Etching both sections did not reveal any additional crack depth as sometimes occurs in metallographic studies of stress-corrosion cracking. Historical Version s – view previous versions of standard. The weld and HAZ of the finned tube appeared to have more cracks than the base metal, and the cracks appear to nearly connect from fin to fin.